    防火板開裂變形原因及其解決方法?

    來源:http://qdlaojing.cn/ 日期:2021-03-12 發(fā)布人:admin
    防火板的變形表現(xiàn)的形式有收縮變形,厚度和密度偏差級結(jié)構(gòu)不對稱所造成的翹曲變形。變形影響建筑功能和使用效果,今天我們來了解一下有哪些原因造成產(chǎn)品變形以及解決的方法。
    The deformation forms of fireproof board include shrinkage deformation, warpage deformation caused by thickness and density deviation and structural asymmetry. Deformation affects the building function and use effect. Today, let's find out what causes the product deformation and the solutions.
    1,過多過大的用水量
    1. Excessive water consumption
    水分過多使用會使組合物料漿堿度過度降低,加速了水鎂石氫氧化鎂的形成,抑制了5.1.8相的生成,導致不能獲得應(yīng)有的力學性能和化學性能水鎂石不是形成穩(wěn)定性能的膠凝相,另外多余的水要排逸出去。如果這樣排濕度不能均速,排濕不一致其收縮也不一致。收縮應(yīng)力會造成制品的變形。
    Excessive use of water will make the alkalinity of the combined material slurry excessively reduce, accelerate the formation of magnesium hydroxide in brucite, inhibit the formation of 5.1.8 phase, resulting in the failure to obtain due mechanical and chemical properties. Brucite is not a stable cementitious phase, and the excess water will be discharged. If the humidity can not be discharged at the same speed in this way, the shrinkage will be different if the humidity is not discharged at the same time. Shrinkage stress can cause deformation of products.
    解決方法:正確的是一般在混合料中液/固比值在0.43~0.47,根據(jù)活性MgO的含量確定MgCl2的用量。同時應(yīng)設(shè)置干燥設(shè)備,使制品的含水率在出廠前控制在8%~10%,避免在使用過程中因排濕的不一致所造成的變形。在實際生產(chǎn)中對于組分中的輕質(zhì)、松軟的填充料應(yīng)盡可能的少加或者不加。這類填充料對抵制材料的收縮不力,同時本身的吸潮性也大,加劇了材料的收縮,同時在組分中也應(yīng)注意纖維的加筋量是否以提高抗擊和防裂要求。
    Solution: it is correct to determine the amount of MgCl2 according to the content of active MgO when the liquid / solid ratio of mixture is 0.43 ~ 0.47. At the same time, the drying equipment should be set to control the moisture content of the products at 8% ~ 10% before leaving the factory, so as to avoid the deformation caused by the inconsistency of moisture removal in the process of use. In actual production, the light and soft fillers should be added as little or no as possible. This kind of filler has poor shrinkage resistance to the material, and its moisture absorption is also large, which aggravates the shrinkage of the material. At the same time, attention should be paid to whether the amount of fiber reinforcement in the components can improve the requirements of resistance and crack prevention.
                   富美家防火板
    2,厚度密度公差大和結(jié)構(gòu)不對稱
    2. Large thickness and density tolerance and asymmetric structure
    這種現(xiàn)象多發(fā)生在手工成型時,因為人為的不穩(wěn)定性因素會照成厚度公差超過板材名義厚度10%板材的容重公差超過6%,這樣造成板材的內(nèi)應(yīng)力偏差大而造成變形。另外因素是增強的玻璃纖維網(wǎng)格布分不均勻,其在制品中的分布位置不對稱也會造成結(jié)構(gòu)應(yīng)力引起變性。
    This phenomenon often occurs in manual forming, because the artificial instability factors will make the thickness tolerance exceed 10% of the nominal thickness of the plate, and the volume weight tolerance of the plate exceed 6%, which will cause large internal stress deviation and deformation of the plate. The other factor is the uneven distribution of the reinforced glass fiber grid, and the asymmetric distribution of the reinforced glass fiber in the product will also cause the structural stress to cause the deformation.
    解決方法:正確的是要注意作為填充的集料比重力應(yīng)盡可能和輕燒氧化鎂粉相一致,避免集料的比重不同造成型過程中成產(chǎn)沉積或上浮于混合料中,造成容重差異大,板材內(nèi)部的收縮、膨脹不一致,產(chǎn)生結(jié)構(gòu)應(yīng)力引起翹曲變形。在使用過程中當外界溫度和溫度發(fā)生變化時,板材因容重的差異大,致在使用過程中吸濕和排濕行為不一致,收縮與膨脹也不一致也會造成變形。因此,克服厚度公差,容重公差和注重結(jié)構(gòu)的對稱性是防止變形的關(guān)鍵舉措。
    Solution: it is correct to pay attention to that the specific gravity of the filled aggregate should be consistent with that of the light burned magnesia powder as far as possible, so as to avoid that the different specific gravity of the aggregate will cause deposition or floating in the mixture during the molding process, resulting in large difference in unit weight, different shrinkage and expansion inside the plate, resulting in structural stress and warping deformation. In the process of use, when the external temperature and temperature change, due to the large difference of bulk density, the moisture absorption and moisture removal behavior are not consistent in the process of use, and the shrinkage and expansion are not consistent, which will also cause deformation. Therefore, to overcome the thickness tolerance, volume weight tolerance and pay attention to the symmetry of the structure are the key measures to prevent deformation.
    以上就是我公司技術(shù)人員給您介紹的防火板變形原因及其解決方法,希望能對您有所幫助,如您想要了解更多資訊內(nèi)容請點擊:富美家防火板http://qdlaojing.cn。
    The above is my company's professional and technical personnel to introduce you to the fire board deformation reasons and solutions, hope to help you, if you want to know more information, please click: fumika fire board http://qdlaojing.cn .

    Related products相關(guān)產(chǎn)品

    聯(lián)系我們

    產(chǎn)品銷售熱線:13165128506

    技術(shù)方案咨詢:18560211715 18663705616

    倉庫地址:山東省濟南市天橋區(qū)金鑫產(chǎn)業(yè)園303倉庫

    九江工廠:九江市江東大道3號

    臺灣新竹工廠:臺灣新竹

    泰國曼谷工廠:泰國曼谷

    關(guān)注我們
    山東創(chuàng)圖建筑裝飾工程有限公司 備案號:魯ICP備14019259號-2 網(wǎng)站地圖 XML TXT 魯公網(wǎng)安備37010502002020號

    截屏,微信識別二維碼

    微信號:13165128506

    欧美日韩精品一区二区不卡| 亚洲国产综合专区久久精品| 丰满少妇,粗大猛烈进高清播报| 色婷一区久久| 久久精品中文在线| 伊人九九精品| 国产精品女久久久久AV爽| 夜夜嗨性色| 欧美亚洲图片视频网站| 中文精品字幕一区| 日本黄a三级三级三级| 亚欧色播激情综合| 日韩图区国产图区欧美图区| 天天色天天摸天天操| 激情小说激情视频乱人伦| 亚洲午夜色情电影网| 久久综合影院大香蕉亚洲| 二区日韩欧美| 69伦理精彩视频| 日本一区二区三区精品久久久| 日本欧美久久视频| 色老头| 国产 欧美 日韩 精品 色| 操逼了美女| 伊人色综合久久久| 亚洲午夜激| 久久妊娠美乳人妻强行内射中出| 日韩欧美色色| 精品色婷婷AV| 麻豆 视频在线观看免费网| 国产日韩中文字幕高清无码视频| 日本无毛亚洲精品 | 丁香五月婷婷成人网| 干进去综合网| 日韩美女免费泡妞网站| 精品少妇AV二区三区| 双插三通群交麻豆| 日韩99视频!在线| 亚洲国产中文不卡在线观看| 操BAⅤ视频| 国产成人无码流出|